410s Stainless Steel Sheet

Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general purpose 12% chromium martensitic stainless steel.

Classification ：

Stainless Steel Plate

+8613176025308

business@sdhmsteel.com

E-mail

Pipe Standards

Product message

Product Details

Product Information

Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden. 410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. 410S is completely ferritic in the annealed condition. It exhibits adequate corrosion resistance similar to 410 and good oxidation resistance.

Standard	ASTM,AISI,SUS,JIS,EN,DIN,BS,GB
Material	201/202/301/302/304/304L/316/316L/309S/310S/321/409/ 410/420/430/430A/434/444/2205/904L etc.
Finish(Surface)	No.1/2B/NO.3/NO.4/BA/HL/Mirror
Technique	Cold Rolled / Hot Rolled
Thickness	0.3mm-3mm(cold rolled) 3-120mm (hot rolled)
Width	1000mm-2000mm or custom
Length	1000mm-6000mm or custom
Application	Stainless steel sheets can apply to construction field, ships building industry, petroleum & chemical industries, war and electricity industries, food processing and medical industry, boiler heatexchanger, machinery and hardware fields. Stainless steel sheet can be made accordingto the customer's requirements. Fast delivery. Quality assured.Welcome to order.

Technical data

Martensitic stainless steel sheets AISI 410

Chemical Composition of 410
Grade	The Element (%)
Grade	C	Si	Mn	P	S	Cr
410	0.08 - 0.15	≤1.00	≤1.00	≤0.035	≤0.030	11.50 - 13.50

Equivalent Materials

Grade	GB	DIN	AISI	JIS
	1Cr13	1.4006	410	SUS410

410S is annealed, or softened, to make it less brittle. This is done by heating it to between 1600 – 1650°F (871 – 899°C), then air cooling it slowly at room temperature to relieve cold-working stresses.

Sometimes, if excessive large grains are encountered after annealing mildly cold-worked material, the annealing temperature should be decreased to a range of 1200 – 1350°F (649 – 732°C) range. However, it should never be increased to 2000°F (1093°C) or above due to embrittlement, which is the partial or complete loss of the material’s ductility, the opposite of the desired result of annealing 410S.

For maximum corrosion resistance to chemical environments, the 410S surface should be free of all heat tint or oxide formed during the annealing or hot working process. It is essential that all traces of oxide and surface decarburization be removed by grounding or polishing all surfaces. Afterwards, parts are immersed in a 10% to 20% nitric acid solution followed by a water rinse. This is to ensure the removal of any residual Iron.

After this step, stainless steel 410S parts are generally considered able to undergo welding by common fusion and resistance techniques, though special attention is paid in order to avoid brittle weld fractures during fabrication and to minimize discontinuities.

The main difference between stainless steel 410 and 410S is that 410 is a basic, general purpose, martensitic stainless steel that can be hardened whereas 410S is a lower Carbon modification of 410 stainless steel, more easily welded but possessing reduced mechanical properties. 410S stainless steel can be easily formed by drawing, spinning, bending, and roll forming.

pplications using 410S Chromium ferritic stainless steel have considerably increased in recent years in chemical industries as well as oil or gas transportation industries. Experiments to determine phase transformation temperatures are ongoing to determine the alpha to gamma transformation temperatures for this alloy in different cooling conditions. Results will determine how 410S can be best used in these industries.

Factory profile

Adhering to the tenet of "integrity first, quality for survival", the company has established a complete marketing channel of "based in North China, radiating the whole country, and facing the world", and has not only established a solid strategic partnership with many domestic and foreign enterprises.We have been committed to product development, production and sales, after more than ten years of efforts, our products have been widely used in various fields.

Packing method: Packing according to customer's requirement.

The company has more than 110,000 square meters of production and processing base, fully introduced the international advanced modern automatic production and processing equipment, and took the lead in passing the ISO9001, TS16949, BV, SGS and other international well-known institutions certification.The products are mainly exported to Italy, Mexico, South Korea, Israel, Turkey, India, Pakistan, Kyrgyzstan, Oman, Kazakhstan, Vietnam, Myanmar and other countries. The company's supply is sufficient, the variety is complete, order production is fast, welcome domestic and foreign manufacturers, traders to contact us.

Company Advantages
1. We are a large-scale production enterprise integrating production, research and development, and can customize the products required by customers.
2. We have a perfect after-sales service system, which can track the problems encountered by customers in production at any time and provide corresponding technical support, so as to share our high-quality resources with customers.
3. After more than ten years of development, the company has complete product varieties and large inventory, which can be delivered in the shortest time.
4. Free samples are available.
5. With obvious price advantage, the company has complete production process, from raw materials to finished products integrated production can maximize the cost savings.